Hastelloy™ C Material Property Data Sheet
Do you need custom fasteners created with Hastelloy™ C? Since our inception, Vegas Fastener Manufacturing has met every challenge of providing
Quality, Timely, Cost-effective solutions for specialty fastener applications. Every product is built to your specifications, using your prints if necessary.
Below are the technical specifications of the Hastelloy™ C Bar Stock we have available to meet your needs.
| |
Hastelloy® C-2000™ alloy, 0.500 inch thick
Subcategory: Metal; Nickel Base; Superalloy
| Component | Wt. % |  | | | C | Max 0.01 | | | Cr | 23 | | | Cu | 1.6 | | | Mo | 16 | | | Ni | 59 | | | Si | Max 0.08 | |
|
Material Notes:
Ni content to balance. Outstanding resistance to oxidizing media, superior resistance to reducing environments. Data provided by the manufacturer, Haynes International, Inc.
| Physical Properties | Metric | English | Comments |
|
| Density | 8.5 g/cc | 0.307 lb/in³ | at RT |
Mechanical Properties |
|
| Tensile Strength, Ultimate | 758 MPa | 110000 psi | |
| Tensile Strength, Yield | 345 MPa | 50000 psi | at 0.2% offset |
| Elongation at Break | 68 % | 68 % | in 50.8 mm |
Electrical Properties |
|
| Electrical Resistivity | 0.000128 ohm-cm | 0.000128 ohm-cm | RT |
| Electrical Resistivity at Elevated Temperature | 0.000129 ohm-cm | 0.000129 ohm-cm | 100°C (212°F) |
| Electrical Resistivity at Elevated Temperature | 0.000131 ohm-cm | 0.000131 ohm-cm | 300°C (570°F) |
| Electrical Resistivity at Elevated Temperature | 0.000132 ohm-cm | 0.000132 ohm-cm | 900°C (1650°F) |
| Electrical Resistivity at Elevated Temperature | 0.000134 ohm-cm | 0.000134 ohm-cm | 700°C (1290°F) |
| Electrical Resistivity at Elevated Temperature | 0.000134 ohm-cm | 0.000134 ohm-cm | 500°C (9300°F) |
Thermal Properties |
|
| CTE, linear 250°C | 12.4 µm/m-°C | 6.89 µin/in-°F | 25-100°C (77-212°F) |
| CTE, linear 250°C | 12.6 µm/m-°C | 7 µin/in-°F | 25-300°C (77-570°F) |
| CTE, linear 500°C | 13.2 µm/m-°C | 7.33 µin/in-°F | 25-500°C (77-930°F) |
| CTE, linear 500°C | 14 µm/m-°C | 7.78 µin/in-°F | 25-700°C (77-1290°F) |
| CTE, linear 1000°C | 15 µm/m-°C | 8.33 µin/in-°F | 25-900°C (77-1650°F) |
| Thermal Conductivity | 9.1 W/m-K | 63.2 BTU-in/hr-ft²-°F | RT |
| Thermal Conductivity at Elevated Temperature | 10.8 W/m-K | 75 BTU-in/hr-ft²-°F | 100°C (212°F) |
| Thermal Conductivity at Elevated Temperature | 14.1 W/m-K | 97.9 BTU-in/hr-ft²-°F | 300°C (570°F) |
| Thermal Conductivity at Elevated Temperature | 18 W/m-K | 125 BTU-in/hr-ft²-°F | 500°C (930°F) |
| Thermal Conductivity at Elevated Temperature | 24.8 W/m-K | 172 BTU-in/hr-ft²-°F | 700°C (1290°F) |
| Thermal Conductivity at Elevated Temperature | 25.9 W/m-K | 180 BTU-in/hr-ft²-°F | 900°C (1650°F) |
|
|
|
This information is provided by
MatWeb.com, The Online Materials Database and is reprinted with their permission.
Copyright 1996-2005 by Automation Creations, Inc.
The contents, results, and technical data on this page may not
be reproduced either electronically, photographically or substantively without permission from
Automation Creations, Inc and MatWeb.com. No warranty, neither expressed nor implied, is given
regarding the accuracy of this information. The user assumes all risk and liability in connection with the use of
information from MatWeb.com.
|
|
|