Material Category: Others

17-7PH

17-7 PH Stainless Steel, CH900, wire

Subcategories: Stainless Steel; Precipitation Hardening Stainless; T S10000 Series Stainless Steel

Close Analogs:

Key Words: UNS S17700, double treatment alloy, CH900, wire, 17-7PH, 17-7 PH, 17/7PH, 17/7 PH, Precipitation Hardening, ASTM A313, ASTM A313M, ASTM A555, ASTM A555M, AMS 5678D, AMS 2241L

Component Weight %
Al 0.75-1.5
C Max 0.090
Cr 16-18
Fe 70.6-76.8
Mn Maz 1.0
Ni 6.5-7.75
P 0.040
Si Max 1.0
S Max 0.040
Physical Properties Metric English Comments Cold Head Hot Forge Wire Form
Density 7.80 g/cc 0.282 lb/in³
Mechanical Properties Metric English Comments Cold Head Hot Forge Wire Form
Tensile Strength, Ultimate 1585 – 2515 MPa 229900 – 364800 psi Depending on temper
Modulus of Elasticity 204 GPa 29600 ksi
Electrical Properties Metric English Comments Cold Head Hot Forge Wire Form
Electrical Resistivity 0.0000830 ohm-cm 0.0000830 ohm-cm
Thermal Properties Metric English Comments Cold Head Hot Forge Wire Form
CTE, linear 11.0 µm/m-°C 6.11 µin/in-°F
@Temperature 0.000 – 100 °C @Temperature 32.0 – 212 °F
11.6 µm/m-°C 6.44 µin/in-°F
@Temperature 0.000 – 315 °C @Temperature 32.0 – 599 °F
Specific Heat Capacity 0.460 J/g-°C 0.110 BTU/lb-°F
@Temperature 0.000 – 100 °C @Temperature 32.0 – 212 °F
Thermal Conductivity 16.4 W/m-K 114 BTU-in/hr-ft²-°F
@Temperature 100 °C @Temperature 212 °F
21.8 W/m-K 151 BTU-in/hr-ft²-°F
@Temperature 500 °C @Temperature 932 °F
Melting Point 1400 – 1450 °C 2550 – 2640 °F
Solidus 1400 °C 2550 °F
Liquidus 1450 °C 2640 °F

17-4PH

Cast Stainless Steel 17- 4, UNS J92150

Subcategories: Stainless Steel; Cast Stainless Steel

Close Analogs:

Key Words:  17-4PH, 17-4 PH, 17/4PH, 17/4 PH; UNS J92150

Component Weight %
C Max 0.080
Cr 15.5-17.5
Cu 3.0-5.0
Fe 70.3-78.5
Mn Max 1.0
Ni 3.0-5.0
P Max 0.040
Si Max 1.0
S Max 0.040

H13

Do you need custom fasteners created with Steel Specials H13? Since our inception, Vegas Fastener Group has met every challenge of providing Quality, Timely, Cost-effective solutions for specialty fastener applications. Every product is built to your specifications, using your prints if necessary.

Below are the technical specifications of the Steel Specials H13 Bar Stock we have available to meet your needs.

AISI Type H13 Hot Work Tool Steel, air or oil quenched from 995-1025°C

Subcategory: Hot Work Steel; Metal; Tool Steel

Key Words: UNS T20813, ASTM A681, FED QQ-T-570, BS 4659 BH13, BS 4659 H13, BS EN ISO 4957 :2000 X40CrMoV5-1, Werkstoff 1.2344

Component Wt. %
C 0.32 – 0.4
Cr 5.13 – 5.25
Fe Min 90.95
Mo 1.33 – 1.4
Si 1
V 1

Material Notes:
Iron content is calculated as a remainder. High hardenability, excellent wear resistance and hot toughness. H13 has good thermal shock resistance and will tolerate some water cooling in service. Nitriding will improve hardness, but can diminish shock resistance if hardened layer is too thick. Electroslag Remelted (ESR) H13 has greater homogeneity and an exceptionally fine structure, resulting in improved machinability, polishability and high temperature tensile strength.

Applications: hot work applications: pressure die casting tools, extrusion tools, forging dies, hot shear blades, stamping dies, plastic molds. ESR H13 is great for aluminium die-casting tools and pastic mold tools requiring a very high polish.

Weldability: Pre and Post-heating recommended, can be welded with oxy-acetylene, inert shielded gas and shielded metal arc; Filler should be similar to the base metal.

Physical Properties Metric English Comments
Density 7.8 g/cc 0.282 lb/in³
Mechanical Properties
Hardness, Knoop 570 570 Converted from Rockwell C Hardness.
Hardness, Rockwell C 52 – 54 52 – 54 air or oil quenched and tempered at 510°C (950°F) and 540°C (1000°F).
Hardness, Rockwell C 51 – 53 51 – 53 air or oil quenched and tempered at 565°C (1050°F).
Hardness, Rockwell C 49 – 51 49 – 51 air or oil quenched and tempered at 595°C (1100°F).
Hardness, Rockwell C 45 – 47 45 – 47 air or oil quenched and tempered at 620°C (1150°F).
Hardness, Rockwell C 39 – 41 39 – 41 air or oil quenched and tempered at 650°C (1200°F).
Hardness, Rockwell C 31 – 33 31 – 33 air or oil quenched and tempered at 675°C (1250°F).
Hardness, Rockwell C 28 – 30 28 – 30 air or oil quenched and tempered at 705°C (1300°F).
Hardness, Rockwell C 51 – 53 51 – 53 air quenched from 1025°C (1875°F) or oil quenched from 1010°C (1850°F) with no temper, or tempered for 1 hour at 315°C (600°F), 425°C (800°F), and 480°C (900°F).
Hardness, Vickers 549 549 Converted from Rockwell C Hardness.
Tensile Strength, Ultimate 1990 MPa 289000 psi
Tensile Strength, Yield 1650 MPa 239000 psi
Elongation at Break 9 % 9 %
Modulus of Elasticity 210 GPa 30500 ksi at 20°C
Bulk Modulus 140 GPa 20300 ksi Typical for steel.
Poisson’s Ratio 0.3 0.3 Calculated
Machinability 50 % 50 % Based on 1% carbon steel. as 100% machinability
Shear Modulus 81 GPa 11700 ksi Estimated from elastic modulus
Thermal Properties
CTE, linear 20°C 11 µm/m-°C 6.11 µin/in-°F 25 – 95°C
CTE, linear 250°C 11.5 µm/m-°C 6.39 µin/in-°F 25 – 205ºC
CTE, linear 500°C 12.4 µm/m-°C 6.89 µin/in-°F 25 – 540°C
Heat Capacity 0.46 J/g-°C 0.11 BTU/lb-°F from 0-100°C (32-212°F)
Thermal Conductivity 24.3 W/m-K 169 BTU-in/hr-ft²-°F at 215°C; 24.4 W/m-K at 350°C, 24.3 at 475°C; 24.7 at 605°C
Descriptive Properties
Annealing Temperature 850 – 870°C for 4 hours furnace cool 20°C per hour max.
Stress Relieving Temperature 600 – 650°C for 2 hours (approx.) cool in still air; always stess relief before hardening.

References are available for this material.

H11

Do you need custom fasteners created with Steel Specials H11? Since our inception, Vegas Fastener Group has met every challenge of providing  Quality, Timely, Cost-effective solutions for specialty fastener applications. Every product is built to your specifications, using your prints if necessary.

Below are the technical specifications of the Steel Specials H11 Bar Stock we have available to meet your needs.

AISI Type H11 Hot Work Tool Steel, air or oil quenched from 995-1025°C

Subcategory: Hot Work Steel; Metal; Tool Steel

Close Analogs: AISI Type H13

Key Words: UNS T20811

Component Wt. %
C 0.33 – 0.43
Cr 5.2
Fe 93
Mo 1.35
V 0.45

Material Notes:

High hardenability, excellent toughness

Physical Properties Metric English Comments
Density 7.8 g/cc 0.282 lb/in³
Mechanical Properties
Hardness, Knoop 642 642 Converted from Rockwell C hardness.
Hardness, Rockwell C 56 56
Hardness, Vickers 621 621
Tensile Strength, Ultimate 1990 MPa 289000 psi
Tensile Strength, Yield 1650 MPa 239000 psi
Elongation at Break 9 % 9 % in 50 mm
Modulus of Elasticity 210 GPa 30500 ksi
Bulk Modulus 140 GPa 20300 ksi Typical for steel.
Poisson’s Ratio 0.3 0.3 Calculated
Charpy Impact 18 J 13.3 ft-lb V-notch
Machinability 45 – 55 % 45 – 55 % Based on 1% carbon steel. as 100% machinability
Shear Modulus 81 GPa 11700 ksi Estimated from elastic modulus
Thermal Properties
CTE, linear 20°C 11 µm/m-°C 6.11 µin/in-°F 25 – 95ºC
CTE, linear 250°C 12.4 µm/m-°C 6.89 µin/in-°F 25 – 540ºC
Heat Capacity 0.46 J/g-°C 0.11 BTU/lb-°F from 0-100°C (32-212°F)
Thermal Conductivity 24.6 W/m-K 171 BTU-in/hr-ft²-°F at 215ºC

References are available for this material.

B16

Do you need custom fasteners created with Steel Specials B16? Since our inception, Vegas Fastener Group has met every challenge of providing
Quality, Timely, Cost-effective solutions for specialty fastener applications. Every product is built to your specifications, using your prints if necessary.

Below are the technical specifications of the Steel Specials B16 Bar Stock we have available to meet your needs.

Component Wt. %
Carbon 0.36 – 0.44
Manganese 0.45 – 0.70
Phosphorus, max 0.035
Sufur, max 0.040
Silicon 0.15-0.35
Chromium 0.80-1.15
Molybdenum 0.50-0.65
Vanadium 0.25-0.35

 

Mechanical Properties Minimum Comments
Tensile Strength, ksi 125 ksi
110 ksi
100 ksi		 up to 2 1/2
2 1/2 – 4
4 – 7
Tensile Strength .02% Offset, ksi 105 ksi
95 ksi
85 ksi		 up to 2 1/2
2 1/2 – 4
4 – 7
Elongation at Break 18 %
17 %
16 %		 up to 2 1/2
2 1/2 – 4
4 – 7
Reduction of Area 50 %
45 %
45 %		 up to 2 1/2
2 1/2 – 4
4 – 7

B7

Do you need custom fasteners created with Steel Specials B7? Since our inception, Vegas Fastener Group has met every challenge of providing
Quality, Timely, Cost-effective solutions for specialty fastener applications. Every product is built to your specifications, using your prints if necessary.

Below are the technical specifications of the Steel Specials B7 Bar Stock we have available to meet your needs.

Component Wt. %
Carbon 0.37 – 0.49
Manganese 0.65 – 1.10
Phosphorus, max 0.035
Sulfur, max 0.040
Silicon 0.15-0.35
Chromium 0.75-1.20
Molybdenum 0.15-0.25

 

Mechanical Properties Minimum
Tensile Strength, ksi 125 ksi
Tensile Strength .02% Offset, ksi 105 ksi
Elongation at Break 16 %
Reduction of Area 50 %

Silicon Bronze 655

Do you need custom fasteners created with Silicon Bronze 655? Since our inception, Vegas Fastener Group has met every challenge of providing
Quality, Timely, Cost-effective solutions for specialty fastener applications. Every product is built to your specifications, using your prints if necessary.

Below are the technical specifications of the Silicon Bronze 655 Bar Stock we have available to meet your needs.

Herculoy®, High-Silicon Bronze A, UNS C65500, H06 (50%) Temper rod

Subcategory: Bronze; Copper Alloy; Metal; Nonferrous Metal Key Words: HCDA 655, CS101, ISO CuSi3Mn1, CEN CS101, copper-silicon, silicon bronze

Component Wt. %
Cu 97
Fe Max 0.8
Mn Max 1.5
Ni Max 0.6
Pb Max 0.5
Si 2.8 – 3.8
Zn Max 1.5

Material Notes: Good to excellent corrosion resistance. Excellent hot and cold workability. Fabricated by blanking, drawing, forming and bending, heading and upsetting, hot forging and pressing, roll threading and knurling, shearing, squeezing, and swaging. Applications: hydraulic pressure lines, anchor screws, bolts, cable clamps, cap screws, machine screws, marine hardware, nuts, pole-line hardware, rivets, U-bolts, electrical conduits, heat exchanger tubing, welding rod, propeller shafts.

Test specimen: wire – 2mm diameter.

Physical Properties Metric English Comments
Density 8.53 g/cc 0.308 lb/in³ at 20°C (68°F)
Mechanical Properties
Hardness, Rockwell B 95 95
Tensile Strength, Ultimate 745 MPa 108000 psi
Tensile Strength, Yield 415 MPa 60200 psi 0.5% extension under load
Elongation at Break 13 % 13 % In 50 mm
Modulus of Elasticity 105 GPa 15200 ksi
Poisson’s Ratio 0.346 0.346
Machinability 30 % 30 % UNS C36000 (free-cutting brass) = 100%
Shear Modulus 39 GPa 5660 ksi
Shear Strength 425 MPa 61600 psi
Electrical Properties
Electrical Resistivity 2.46e-005 ohm-cm 2.46e-005 ohm-cm at 20°C (68°F)
Thermal Properties
CTE, linear 250°C 18 µm/m-°C 10 µin/in-°F from 20-300°C (68-570°F)
Heat Capacity 0.38 J/g-°C 0.0908 BTU/lb-°F
Thermal Conductivity 36 W/m-K 250 BTU-in/hr-ft²-°F
Melting Point 970 – 1025 °C 1780 – 1880 °F
Solidus 970 °C 1780 °F
Liquidus 1025 °C 1880 °F
Processing Properties
Annealing Temperature 475 – 700 °C 887 – 1290 °F
Hot-Working Temperature 700 – 875 °C 1290 – 1610 °F
Recrystallization Temperature 4.44 °C 40 °F C37700 (forging brass) = 100%

References are available for this material.

 

Silicon Bronze 651

Do you need custom fasteners created with Silicon Bronze 651? Since our inception, Vegas Fastener Group has met every challenge of providing Quality, Timely, Cost-effective solutions for specialty fastener applications. Every product is built to your specifications, using your prints if necessary.

Below are the technical specifications of the Silicon Bronze 651 Bar Stock we have available to meet your needs.

Low-silicon bronze B, UNS C65100, OSO35 Temper rod

Subcategory: Bronze; Copper Alloy; Metal; Nonferrous Metal Key Words: CDA 651, ISO CuSi1, CEN C115C

Component Wt. %
Cu 98.5
Fe Max 0.8
Mn Max 0.7
Pb Max 0.05
Si 0.8 – 2
Zn Max 1.5

Material Notes: Good to excellent corrosion resistance. Excellent hot and cold workability. Fabricated by forming and bending, heading and upsetting, hot forging and pressing, roll threading and knurling, squeezing and swaging. Applications: hydraulic pressure lines, anchor screws, bolts, cable clamps, cap screws, machine screws, marine hardware, nuts, pole-line hardware, rivets, U-bolts, electrical conduits, heat exchanger tubing, welding rod.

Test specimen: rod – 25mm diameter.

Physical Properties Metric English Comments
Density 8.75 g/cc 0.316 lb/in³ at 20°C (68°F)
Mechanical Properties
Hardness, Rockwell F 55 55
Tensile Strength, Ultimate 275 MPa 39900 psi
Tensile Strength, Yield 105 MPa 15200 psi 0.5% extension under load
Elongation at Break 50 % 50 % In 50 mm
Modulus of Elasticity 115 GPa 16700 ksi
Machinability 30 % 30 % UNS C36000 (free-cutting brass) = 100%
Shear Modulus 44 GPa 6380 ksi
Electrical Properties
Electrical Resistivity 1.44e-005 ohm-cm 1.44e-005 ohm-cm
Thermal Properties
CTE, linear 250°C 18 µm/m-°C 10 µin/in-°F from 20-300°C (68-570°F)
Heat Capacity 0.38 J/g-°C 0.0908 BTU/lb-°F
Thermal Conductivity 57 W/m-K 396 BTU-in/hr-ft²-°F at 20°C (68°F)
Melting Point 1030 – 1060 °C 1890 – 1940 °F
Solidus 1030 °C 1890 °F
Liquidus 1060 °C 1940 °F
Processing Properties
Annealing Temperature 475 – 675 °C 887 – 1250 °F
Hot-Working Temperature 700 – 875 °C 1290 – 1610 °F

References are available for this material.

 

Phosphorous Bronze 510

Do you need custom fasteners created with Phosphorous Bronze 510? Since our inception, Vegas Fastener Group has met every challenge of providing Quality, Timely, Cost-effective solutions for specialty fastener applications. Every product is built to your specifications, using your prints if necessary.

Below are the technical specifications of the Phosphorous Bronze 510 Bar Stock we have available to meet your needs.

Phosphor bronze 8% C, UNS C52100, H02 Temper rod

Subcategory: Bronze; Copper Alloy; Metal; Nonferrous Metal Key Words: CDA 521, PB104, ISO CuSn8P

Component Wt. %
Cu 90.5 – 92.8
Fe Max 0.1
P 0.03 – 0.35
Pb Max 0.05
Sn 7 – 9
Zn Max 0.2

Material Notes: Good to excellent corrosion resistance. Good cold workability for blanking, drawing, forming and bending, shearing and stamping. Applications: more severe service conditions than C51000.

Trace content of Phosphorus.

Test specimen: rod – 13mm diameter.

Physical Properties Metric English Comments
Density 8.8 g/cc 0.318 lb/in³ at 20°C (68°F)
Mechanical Properties
Hardness, Rockwell B 85 85
Tensile Strength, Ultimate 550 MPa 79800 psi
Tensile Strength, Yield 450 MPa 65300 psi
Elongation at Break 33 % 33 % in 50 mm
Modulus of Elasticity 110 GPa 16000 ksi
Poisson’s Ratio 0.341 0.341
Machinability 20 % 20 % UNS C36000 (free-cutting brass) = 100%
Shear Modulus 41 GPa 5950 ksi
Electrical Properties
Electrical Resistivity 1.33e-005 ohm-cm 1.33e-005 ohm-cm at 20°C (68°F)
Thermal Properties
CTE, linear 250°C 18.2 µm/m-°C 10.1 µin/in-°F from 20-300°C (68-570°F)
Heat Capacity 0.38 J/g-°C 0.0908 BTU/lb-°F
Thermal Conductivity 62 W/m-K 430 BTU-in/hr-ft²-°F at 20°C (68°F)
Melting Point 880 – 1025 °C 1620 – 1880 °F
Solidus 880 °C 1620 °F
Liquidus 1025 °C 1880 °F
Processing Properties
Annealing Temperature 475 – 675 °C 887 – 1250 °F

 

Naval Brass 464

Do you need custom fasteners created with Naval Brass 464? Since our inception, Vegas Fastener Group has met every challenge of providing Quality, Timely, Cost-effective solutions for specialty fastener applications. Every product is built to your specifications, using your prints if necessary.

Below are the technical specifications of the Naval Brass 464 Bar Stock we have available to meet your needs.

Uninhibited Naval brass, UNS C46400

Subcategory: Brass; Copper Alloy; Metal; Nonferrous Metal Key Words: CDA 464, CZ133, CZ113, ISO CuZn39Sn1, CEN CW719R, UNS C46700

Component Wt. %
Cu 59 – 62
Fe Max 0.1
Pb Max 0.2
Sn 0.5 – 1
Zn 39.25

Material Notes: Fair to excellent corrosion resistance. Excellent hot workability and hot forgeability. Fabricated by blanking, drawing, bending, heading and upsetting, hot forging, pressing. Applications: aircraft turnbuckle barrels, balls, bolts, marine hardware, nuts, propeller shafts, rivets, valve stems, condenser plates, welding rod.

Available as flat products, rod, shape, and tube.

Physical Properties Metric English Comments
Density 8.41 g/cc 0.304 lb/in³ at 20°C (68°F)
Mechanical Properties
Tensile Strength, Ultimate 379 – 607 MPa 55000 – 88000 psi
Tensile Strength, Yield 172 – 455 MPa 24900 – 66000 psi Depending on temper
Elongation at Break 50 % 50 % in 431.8 mm.
Modulus of Elasticity 100 GPa 14500 ksi
Poisson’s Ratio 0.28 0.28 Calculated
Machinability 30 % 30 % UNS C36000 (free-cutting brass) = 100%
Shear Modulus 39 GPa 5660 ksi
Thermal Properties
CTE, linear 250°C 21.2 µm/m-°C 11.8 µin/in-°F from 20-300°C (68-570°F)
Thermal Conductivity 116 W/m-K 805 BTU-in/hr-ft²-°F at 20°C (68°F)
Melting Point 885 – 900 °C 1630 – 1650 °F
Solidus 885 °C 1630 °F
Liquidus 900 °C 1650 °F

References are available for this material.

 

Blog Search

Search By Material

Search By Application

Get Started

Contact us for a customized fastener solution.

Speak To An Expert

© 2025 All Rights Reserved.