Hastelloy® C-2000™ alloy, 0.500 inch thick
Subcategory: Metal; Nickel Base; Superalloy
| Component | Wt. % |
| C | Max 0.01 |
| Cr | 23 |
| Cu | 1.6 |
| Mo | 16 |
| Ni | 59 |
| Si | Max 0.08 |
Material Notes: Ni content to balance. Outstanding resistance to oxidizing media, superior resistance to reducing environments.
Data provided by the manufacturer, Haynes International, Inc.
| Physical Properties | Metric | English | Comments |
| Density | 8.5 g/cc | 0.307 lb/in³ | at RT |
| Mechanical Properties | |||
| Tensile Strength, Ultimate | 758 MPa | 110000 psi | |
| Tensile Strength, Yield | 345 MPa | 50000 psi | at 0.2% offset |
| Elongation at Break | 68 % | 68 % | in 50.8 mm |
| Electrical Properties | |||
| Electrical Resistivity | 0.000128 ohm-cm | 0.000128 ohm-cm | RT |
| Electrical Resistivity at Elevated Temperature | 0.000129 ohm-cm | 0.000129 ohm-cm | 100°C (212°F) |
| Electrical Resistivity at Elevated Temperature | 0.000131 ohm-cm | 0.000131 ohm-cm | 300°C (570°F) |
| Electrical Resistivity at Elevated Temperature | 0.000132 ohm-cm | 0.000132 ohm-cm | 900°C (1650°F) |
| Electrical Resistivity at Elevated Temperature | 0.000134 ohm-cm | 0.000134 ohm-cm | 700°C (1290°F) |
| Electrical Resistivity at Elevated Temperature | 0.000134 ohm-cm | 0.000134 ohm-cm | 500°C (9300°F) |
| Thermal Properties | |||
| CTE, linear 250°C | 12.4 µm/m-°C | 6.89 µin/in-°F | 25-100°C (77-212°F) |
| CTE, linear 250°C | 12.6 µm/m-°C | 7 µin/in-°F | 25-300°C (77-570°F) |
| CTE, linear 500°C | 13.2 µm/m-°C | 7.33 µin/in-°F | 25-500°C (77-930°F) |
| CTE, linear 500°C | 14 µm/m-°C | 7.78 µin/in-°F | 25-700°C (77-1290°F) |
| CTE, linear 1000°C | 15 µm/m-°C | 8.33 µin/in-°F | 25-900°C (77-1650°F) |
| Thermal Conductivity | 9.1 W/m-K | 63.2 BTU-in/hr-ft²-°F | RT |
| Thermal Conductivity at Elevated Temperature | 10.8 W/m-K | 75 BTU-in/hr-ft²-°F | 100°C (212°F) |
| Thermal Conductivity at Elevated Temperature | 14.1 W/m-K | 97.9 BTU-in/hr-ft²-°F | 300°C (570°F) |
| Thermal Conductivity at Elevated Temperature | 18 W/m-K | 125 BTU-in/hr-ft²-°F | 500°C (930°F) |
| Thermal Conductivity at Elevated Temperature | 24.8 W/m-K | 172 BTU-in/hr-ft²-°F | 700°C (1290°F) |
| Thermal Conductivity at Elevated Temperature | 25.9 W/m-K | 180 BTU-in/hr-ft²-°F | 900°C (1650°F) |