Do you need custom Hastelloy fasteners created with Hastelloy C 276? Since our inception, Vegas Fastener Group has met every challenge of providing quality, timely, cost-effective solutions for specialty fastener applications. Every product is built to your specifications, using your prints if necessary.
Below are the material properties, composition, and technical specifications of the Hastelloy C276 Bar Stock we have available to meet your needs.
Hastelloy® C 276 alloy
Subcategory: Metal; Nickel Base; Superalloy Key Words: ASME SB-622, ASME SB-626 SCC resistant, flue-gas desulfurization systems, UNS N10276, ASME SB-574, ASME SB-575, ASME SB-619
Component | Wt. % |
C | Max 0.01 |
Co | Max 2.5 |
Cr | 14.5 – 16.5 |
Fe | 4 – 7 |
Mn | Max 1 |
Mo | 15 – 17 |
Ni | 57 |
P | Max 0.025 |
S | Max 0.01 |
Si | Max 0.08 |
V | Max 0.35 |
W | 3 – 4.5 |
Material Notes: Versatile corrosion-resistant alloy, usually does not need to be solution heat treated after welding and has vastly improved fabricability, excellent resistance to localized corrosion and to both oxidizing and reducing media. Resists formation of grain-boundary precipitates and is therefore suitable for chemical process applications in the as-welded condition. C-276 has excellent resistance to strong oxidizers like ferric and cupric chlorides, hot contaminated media (organic and inorganic), chlorine, formic and acetic acids, acetic anhydride, seawater, brine solutions, sulfur compounds, wet chlorine gas, hypochlorite and chlorine dioxide.
Data provided by the manufacturer, Haynes International, Inc.
Physical Properties | Metric | English | Comments |
Density | 8.89 g/cc | 0.321 lb/in³ | at RT |
Mechanical Properties | |||
Hardness, Rockwell B | 90 | 90 | Average room temperature hardness for sheet (average of 49 tests); 87 HRB average room temperature hardness for plate (average of 35 tests) |
Hardness, Vickers | 191 | 191 | Conversion from Rockwell B hardness. |
Tensile Strength, Ultimate | 826.7 MPa | 120000 psi | |
Tensile Strength, Yield | 364.7 MPa | 52900 psi | at 0.2% offset |
Elongation at Break | 59 % | 59 % | in 50.8 mm |
Modulus of Elasticity | 205 GPa | 29700 ksi | RT |
Modulus of Elasticity at Elevated Temperature | 176 GPa | 25500 ksi | heat treated at 1121°C (2050°F) and rapid quenched; 538°C |
Modulus of Elasticity at Elevated Temperature | 182 GPa | 26400 ksi | heat treated at 1121°C (2050°F) and rapid quenched; 427°C |
Modulus of Elasticity at Elevated Temperature | 188 GPa | 27300 ksi | heat treated at 1121°C (2050°F) and rapid quenched; 316°C |
Modulus of Elasticity at Elevated Temperature | 195 GPa | 28300 ksi | heat treated at 1121°C (2050°F) and rapid quenched; 204°C |
Charpy Impact | 357 J | 263 ft-lb | at -196°C solution heat treated at 1121°C (2050°F), rapid quenched; 339 J at -196°C aged 100 hours at 260°C; 130 J at -196°C aged 100 hours at 538°C (1000°F); 87 J at -196°C aged 1000 hours at 538°C (1000°F) |
Electrical Properties | |||
Electrical Resistivity | 0.00013 ohm-cm | 0.00013 ohm-cm | 24°C (75°F) |
Thermal Properties | |||
CTE, linear 20°C | 11.2 µm/m-°C | 6.22 µin/in-°F | 24-93°C (75-200°F) |
CTE, linear 250°C | 12 µm/m-°C | 6.67 µin/in-°F | 24-204°C (75-400°F) |
CTE, linear 500°C | 12.8 µm/m-°C | 7.11 µin/in-°F | 24-316°C (75-600°F) |
CTE, linear 500°C | 13.2 µm/m-°C | 7.33 µin/in-°F | 24-538°C (75-1000°F) |
CTE, linear 500°C | 13.2 µm/m-°C | 7.33 µin/in-°F | 24-427°C (75-800°F) |
Heat Capacity | 0.427 J/g-°C | 0.102 BTU/lb-°F | RT |
Thermal Conductivity | 10.2 W/m-K | 70.8 BTU-in/hr-ft²-°F | 38°C |
Thermal Conductivity | 7.2 W/m-K | 50 BTU-in/hr-ft²-°F | -168°C |
Thermal Conductivity | 8.6 W/m-K | 59.7 BTU-in/hr-ft²-°F | -73°C |
Thermal Conductivity | 9.4 W/m-K | 65.2 BTU-in/hr-ft²-°F | -18°C |
Thermal Conductivity at Elevated Temperature | 11.1 W/m-K | 77 BTU-in/hr-ft²-°F | 93°C |
Thermal Conductivity at Elevated Temperature | 13 W/m-K | 90.2 BTU-in/hr-ft²-°F | 204°C |
Thermal Conductivity at Elevated Temperature | 15 W/m-K | 104 BTU-in/hr-ft²-°F | 316°C |
Thermal Conductivity at Elevated Temperature | 16.9 W/m-K | 117 BTU-in/hr-ft²-°F | 427°C |
Thermal Conductivity at Elevated Temperature | 19 W/m-K | 132 BTU-in/hr-ft²-°F | 538°C |
Melting Point | 1323 – 1371 °C | 2410 – 2500 °F | |
Solidus | 1323 °C | 2410 °F | |
Liquidus | 1371 °C | 2500 °F |