AISI Type 330 Stainless Steel, annealed bar
Subcategory: Heat Resisting; Metal; Stainless Steel; T 300 Series Stainless Steel
Key Words: UNS N08330, AMS 5592, AMS 5716, ASTM B511, ASTM B512, ASTM B535, ASTM B536, ASTM B546, SAE J405 (30330), SAE J412 (30330)
| Component |
Wt. % |
| C |
Max 0.08 |
| Cr |
19 |
| Fe |
42 |
| Mn |
Max 2 |
| Ni |
36 |
| P |
Max 0.04 |
| S |
Max 0.03 |
| Si |
Max 1.13 |
Material Notes:
specimens were 25-75 mm diameter
| Physical Properties |
Metric |
English |
Comments |
|
|
| Density |
8 g/cc |
0.289 lb/in³ |
|
| Mechanical Properties |
|
|
| Hardness, Brinell |
139 |
139 |
Converted from Rockwell B hardness. |
| Hardness, Knoop |
155 |
155 |
Converted from Rockwell B hardness. |
| Hardness, Rockwell B |
80 |
80 |
|
| Hardness, Vickers |
153 |
153 |
Converted from Rockwell B hardness. |
| Tensile Strength, Ultimate |
585 MPa |
84800 psi |
|
| Tensile Strength, Yield |
290 MPa |
42100 psi |
at 0.2% offset |
| Elongation at Break |
45 % |
45 % |
in 50 mm |
| Modulus of Elasticity |
197 GPa |
28600 ksi |
at 21°C, 179 GPa at 315°C, 164 GPa at 540°C, 145 GPa at 760°C, 134 GPa at 870°C, 124 GPa at 980°C |
| Charpy Impact |
325 J |
240 ft-lb |
Annealed |
| Electrical Properties |
|
|
| Electrical Resistivity |
0.000102 ohm-cm |
0.000102 ohm-cm |
at 20°C, 0.000114 Ohm-cm at 425°C |
| Magnetic Permeability |
1.02 |
1.02 |
approximate value for the annealed condition at RT |
| Thermal Properties |
|
|
| CTE, linear 20°C |
14.4 µm/m-°C |
8 µin/in-°F |
from 0-100°C (32-212°F) |
| CTE, linear 250°C |
16 µm/m-°C |
8.89 µin/in-°F |
at 0-315°C (32-600°F) |
| CTE, linear 500°C |
16.7 µm/m-°C |
9.28 µin/in-°F |
at 0-540°C, 17.3 µm/m-C at 0-650°C, 18.0 µm/m-C at 0-870°C |
| Heat Capacity |
0.46 J/g-°C |
0.11 BTU/lb-°F |
from 0-100°C (32-212°F) |
| Thermal Conductivity |
12.5 W/m-K |
86.8 BTU-in/hr-ft²-°F |
at 24°C, 16.3 W/m-K at 100°C, 19.4 W/m-K at 425°C, 21.6 W/m-K at 500°C, 28.5 W/m-K at 870°C |
| Melting Point |
1400 – 1425 °C |
2550 – 2600 °F |
|
| Solidus |
1400 °C |
2550 °F |
|
| Liquidus |
1425 °C |
2600 °F |
|
| Maximum Service Temperature, Air |
1035 °C |
1890 °F |
Intermittent Service |
| Maximum Service Temperature, Air |
1150 °C |
2100 °F |
Continuous Service |
|
References are available for this material.