Stainless Steel 416

Do you need custom fasteners created with Stainless Steel 416? Since our inception, Vegas Fastener Group has met every challenge of providing Quality, Timely, Cost-effective solutions for specialty fastener applications. Every product is built to your specifications, using your prints if necessary.

Below are the technical specifications of the Stainless Steel 416 Bar Stock we have available to meet your needs.

AISI Type 416 Stainless Steel, annealed bar

Subcategory: Heat Resisting; Metal; Stainless Steel; T 400 Series Stainless Steel

Close Analogs: AISI Type 416 Se

Key Words: UNS S41600, ASME SA194, ASTM A194, ASTM A314, ASTM A473, ASTM A581, ASTM A582, FED QQ-W-423, MIL SPEC MIL-S-862, SAE J405(51416), DIN 1.4005, UNI X 12 CrS 13, B.S. 416 S 21, martensitic, ISO 683/13 7

Component Wt. %
C Max 0.15
Cr 13
Fe 84
Mn Max 1.25
Mo Max 0.6
P Max 0.06
S Max 0.15
Si Max 1

Material Notes:
Molybdenum content optional

Physical Properties Metric English Comments
Density 7.8 g/cc 0.282 lb/in³
Mechanical Properties
Hardness, Rockwell B 82 82
Tensile Strength, Ultimate 515 MPa 74700 psi
Tensile Strength, Yield 275 MPa 39900 psi at 0.2% offset
Elongation at Break 30 % 30 % in 50 mm
Modulus of Elasticity 200 GPa 29000 ksi
Shear Modulus 83 GPa 12000 ksi
Electrical Properties
Electrical Resistivity 5.7e-005 ohm-cm 5.7e-005 ohm-cm at 20°C, 0.000108 Ohm-cm at 650°C
Magnetic Permeability 700 – 1000 700 – 1000 annealed condition at RT
Thermal Properties
CTE, linear 20°C 9.9 µm/m-°C 5.5 µin/in-°F from 0-100°C (32-212°F)
CTE, linear 250°C 11 µm/m-°C 6.11 µin/in-°F at 0-315°C (32-600°F)
CTE, linear 500°C 11.5 µm/m-°C 6.39 µin/in-°F 0-540°C, 11.7 at 0-650°C
Heat Capacity 0.46 J/g-°C 0.11 BTU/lb-°F from 0-100°C (32-212°F)
Thermal Conductivity 24.9 W/m-K 173 BTU-in/hr-ft²-°F at 100°C; 28.7 W/m-K at 500°C
Melting Point 1480 – 1530 °C 2700 – 2790 °F
Solidus 1480 °C 2700 °F
Liquidus 1530 °C 2790 °F
Maximum Service Temperature, Air 675 °C 1250 °F Continuous Service
Maximum Service Temperature, Air 760 °C 1400 °F Intermittent Service