Do you need custom fasteners created with Aluminum Bronze? Since our inception, Vegas Fastener Group has met every challenge of providing Quality, Timely, Cost-effective solutions for specialty fastener applications. Every product is built to your specifications, using your prints if necessary.
Below are the technical specifications of the Aluminum Bronze Bar Stock we have available to meet your needs.
Aluminum Bronze, UNS C61300
Subcategory: Bronze; Copper Alloy; Metal; Nonferrous Metal Key Words: CDA 613
| Component | Wt. % |
| Al | 6 – 7.5 |
| Cu | 88.5 – 91.5 |
| Fe | 2 – 3 |
| Mn | Max 0.1 |
| Other | Max 0.05 |
| Pb | Max 0.01 |
| Sn | 0.02 – 0.5 |
| Zn | Max 0.05 |
Material Notes: Good to excellent corrosion resistance. Good hot and cold formability. Fair to poor machinability Applications: nuts, bolts, stringers and threaded members, corrosion resistant vessels and tanks, structural components, machine parts, condenser tube and piping systems, marine protective sheathing and fasteners, munitions mixing troughs and blending chambers.
Properties typical for 13mm thick plate .
| Physical Properties | Metric | English | Comments |
| Density | 7.89 g/cc | 0.285 lb/in³ | at 20°C (68°F); approximately 1.8% volume contraction on freezing |
| Mechanical Properties | |||
| Hardness, Rockwell B | 82 | 82 | O60 temper |
| Hardness, Rockwell B | 91 | 91 | H04 temper |
| Tensile Strength, Ultimate | 540 MPa | 78300 psi | O60 temper |
| Tensile Strength, Ultimate | 585 MPa | 84800 psi | H04 temper |
| Tensile Strength, Yield | 240 MPa | 34800 psi | 0.5% extension, O60 temper |
| Tensile Strength, Yield | 400 MPa | 58000 psi | 0.5% extension, H04 temper |
| Elongation at Break | 35 % | 35 % | in 50 mm, H04 temper |
| Elongation at Break | 42 % | 42 % | in 50 mm, O60 temper |
| Reduction of Area | 25 % | 25 % | H04 temper |
| Reduction of Area | 32 % | 32 % | O60 temper |
| Modulus of Elasticity | 115 GPa | 16700 ksi | |
| Compressive Strength | 825 MPa | 120000 psi | O60 temper |
| Compressive Strength | 860 MPa | 125000 psi | H04 temper |
| Poisson’s Ratio | 0.312 | 0.312 | |
| Charpy Impact | 81 – 88 J | 59.7 – 64.9 ft-lb | Keyhole, at -30 to 150°C |
| Izod Impact | 54 – 66 J | 39.8 – 48.7 ft-lb | at -30 to 150°C |
| Fatigue Strength | 180 MPa | 26100 psi | Reverse bending, at 10^8 cycles |
| Machinability | 30 % | 30 % | Based on 100% machinability for UNS C360000 |
| Shear Modulus | 44 GPa | 6380 ksi | |
| Electrical Properties | |||
| Electrical Resistivity | 1.44e-005 ohm-cm | 1.44e-005 ohm-cm | at 20°C (68°F) |
| Magnetic Permeability | 1.16 | 1.16 | |
| Thermal Properties | |||
| CTE, linear 250°C | 16.2 µm/m-°C | 9 µin/in-°F | from 20-300°C (68-570°F) |
| Heat Capacity | 0.375 J/g-°C | 0.0896 BTU/lb-°F | |
| Thermal Conductivity | 56.5 W/m-K | 392 BTU-in/hr-ft²-°F | at 20°C (68°F) |
| Melting Point | 1040 – 1045 °C | 1900 – 1910 °F | |
| Solidus | 1040 °C | 1900 °F | |
| Liquidus | 1045 °C | 1910 °F | |
| Processing Properties | |||
| Processing Temperature | 1010 °C | 1850 °F | Hot-Shortness Temperature |
| Annealing Temperature | 600 – 875 °C | 1110 – 1610 °F | |
| Hot-Working Temperature | 800 – 925 °C | 1470 – 1700 °F | |
| Recrystallization Temperature | 785 – 870 °C | 1450 – 1600 °F | |
References are available for this material.