Do you need custom fasteners created with Copper CDA 110? Since our inception, Vegas Fastener Group has met every challenge of providing Quality, Timely, Cost-effective solutions for specialty fastener applications. Every product is built to your specifications, using your prints if necessary.
Below are the technical specifications of the Copper CDA 110 Bar Stock we have available to meet your needs.
Electrolytic tough pitch Copper, UNS C11000, OSO50 Temper flat products, rod, tube, shapes
Subcategory: Copper Alloy; Metal; Nonferrous Metal Key Words: ASTM-B-152, QQ-C-576, CDA 110 ETP, C101, ISO Cu-ETP
| Component | Wt. % |
| Cu | 99.9 |
| O | 0.04 |
Material Notes: Good to excellent corrosion resistance. Excellent hot and cold workability; good forgeability. Fabricated by coining, coppersmithing, drawing and upsetting, hot forging and pressing, spinning, swaging, stamping. Applications: downspouts, gutters, roofing, gaskets, auto radiators, busbars, nails, printing rolls, rivets, and radio parts.
Test specimens: flat products – 1mm and 6mm thicknesses, rod – 25mm OD, tube – 25mm OD x 1.65mm wall thickness, and shapes – 13mm section.
| Physical Properties | Metric | English | Comments |
| Density | 7.93 g/cc | 0.286 lb/in³ | Liquid, at 1083°C |
| Density | 8.32 g/cc | 0.301 lb/in³ | Solid, at 1083°C |
| Density | 8.89 g/cc | 0.321 lb/in³ | Solid, at 20°C (68°F) |
| Mechanical Properties | |||
| Hardness, Rockwell F | 40 | 40 | |
| Tensile Strength, Ultimate | 220 MPa | 31900 psi | |
| Tensile Strength, Yield | 69 MPa | 10000 psi | At 0.5% extension under load |
| Elongation at Break | 45 % | 45 % | In 50 mm, 1mm thickness, tube |
| Elongation at Break | 50 % | 50 % | In 50 mm, 6mm thickness, shapes |
| Elongation at Break | 55 % | 55 % | In 50 mm, rod |
| Poisson’s Ratio | 0.33 | 0.33 | |
| Machinability | 20 % | 20 % | UNS C36000 (free-cutting brass) = 100% |
| Shear Strength | 150 MPa | 21800 psi | |
| Coefficient of Friction | 0.29 | 0.29 | Sliding, with cast iron, no lubrication |
| Coefficient of Friction | 0.36 | 0.36 | Sliding, with carbon steel, no lubrication |
| Coefficient of Friction | 0.53 | 0.53 | Sliding, with glass, no lubrication |
| Coefficient of Friction, Static | 0.53 | 0.53 | With carbon steel, no lubrication |
| Coefficient of Friction, Static | 0.68 | 0.68 | With carbon steel, no lubrication |
| Coefficient of Friction, Static | 1.05 | 1.05 | With cast iron, no lubrication |
| Thermal Properties | |||
| Heat of Fusion | 205 J/g | 88.2 BTU/lb | |
| CTE, linear 20°C | 17 µm/m-°C | 9.44 µin/in-°F | from 20-100°C (68-212°F) |
| CTE, linear 100°C | 17.3 µm/m-°C | 9.61 µin/in-°F | from 20-200°C (68-390°F) |
| CTE, linear 250°C | 17.7 µm/m-°C | 9.83 µin/in-°F | from 20-300°C (68-570°F) |
| Heat Capacity | 0.385 J/g-°C | 0.092 BTU/lb-°F | |
| Thermal Conductivity | 388 W/m-K | 2690 BTU-in/hr-ft²-°F | at 20°C (68°F) |
| Melting Point | 1065 – 1083 °C | 1950 – 1980 °F | |
| Solidus | 1065 °C | 1950 °F | Eutectic |
| Liquidus | 1083 °C | 1980 °F | |
| Softening Point | 360 °C | 680 °F | |
| Processing Properties | |||
| Annealing Temperature | 475 – 750 °C | 887 – 1380 °F | |
| Hot-Working Temperature | 750 – 875 °C | 1380 – 1610 °F | |
| Recrystallization Temperature | 18.3 °C | 65 °F | C37700 (forging brass) = 100% |
| Descriptive Properties | |||
| Color | Reddish metallic | ||
References are available for this material.