Uninhibited Naval brass, UNS C46400
Subcategory: Brass; Copper Alloy; Metal; Nonferrous Metal Key Words: CDA 464, CZ133, CZ113, ISO CuZn39Sn1, CEN CW719R, UNS C46700
|Cu||59 – 62|
|Sn||0.5 – 1|
Material Notes: Fair to excellent corrosion resistance. Excellent hot workability and hot forgeability. Fabricated by blanking, drawing, bending, heading and upsetting, hot forging, pressing. Applications: aircraft turnbuckle barrels, balls, bolts, marine hardware, nuts, propeller shafts, rivets, valve stems, condenser plates, welding rod.
Available as flat products, rod, shape, and tube.
|Density||8.41 g/cc||0.304 lb/in³||at 20°C (68°F)|
|Tensile Strength, Ultimate||379 – 607 MPa||55000 – 88000 psi|
|Tensile Strength, Yield||172 – 455 MPa||24900 – 66000 psi||Depending on temper|
|Elongation at Break||50 %||50 %||in 431.8 mm.|
|Modulus of Elasticity||100 GPa||14500 ksi|
|Machinability||30 %||30 %||UNS C36000 (free-cutting brass) = 100%|
|Shear Modulus||39 GPa||5660 ksi|
|CTE, linear 250°C||21.2 µm/m-°C||11.8 µin/in-°F||from 20-300°C (68-570°F)|
|Thermal Conductivity||116 W/m-K||805 BTU-in/hr-ft²-°F||at 20°C (68°F)|
|Melting Point||885 – 900 °C||1630 – 1650 °F|
|Solidus||885 °C||1630 °F|
|Liquidus||900 °C||1650 °F|