Phosphorous Bronze 510

Do you need custom fasteners created with Phosphorous Bronze 510? Since our inception, Vegas Fastener Group has met every challenge of providing Quality, Timely, Cost-effective solutions for specialty fastener applications. Every product is built to your specifications, using your prints if necessary.

Below are the technical specifications of the Phosphorous Bronze 510 Bar Stock we have available to meet your needs.

Phosphor bronze 8% C, UNS C52100, H02 Temper rod

Subcategory: Bronze; Copper Alloy; Metal; Nonferrous Metal Key Words: CDA 521, PB104, ISO CuSn8P

Component Wt. %
Cu 90.5 – 92.8
Fe Max 0.1
P 0.03 – 0.35
Pb Max 0.05
Sn 7 – 9
Zn Max 0.2

Material Notes: Good to excellent corrosion resistance. Good cold workability for blanking, drawing, forming and bending, shearing and stamping. Applications: more severe service conditions than C51000.

Trace content of Phosphorus.

Test specimen: rod – 13mm diameter.

Physical Properties Metric English Comments
Density 8.8 g/cc 0.318 lb/in³ at 20°C (68°F)
Mechanical Properties
Hardness, Rockwell B 85 85
Tensile Strength, Ultimate 550 MPa 79800 psi
Tensile Strength, Yield 450 MPa 65300 psi
Elongation at Break 33 % 33 % in 50 mm
Modulus of Elasticity 110 GPa 16000 ksi
Poisson’s Ratio 0.341 0.341
Machinability 20 % 20 % UNS C36000 (free-cutting brass) = 100%
Shear Modulus 41 GPa 5950 ksi
Electrical Properties
Electrical Resistivity 1.33e-005 ohm-cm 1.33e-005 ohm-cm at 20°C (68°F)
Thermal Properties
CTE, linear 250°C 18.2 µm/m-°C 10.1 µin/in-°F from 20-300°C (68-570°F)
Heat Capacity 0.38 J/g-°C 0.0908 BTU/lb-°F
Thermal Conductivity 62 W/m-K 430 BTU-in/hr-ft²-°F at 20°C (68°F)
Melting Point 880 – 1025 °C 1620 – 1880 °F
Solidus 880 °C 1620 °F
Liquidus 1025 °C 1880 °F
Processing Properties
Annealing Temperature 475 – 675 °C 887 – 1250 °F