Do you need custom fasteners created with Silicon Bronze 651? Since our inception, Vegas Fastener Group has met every challenge of providing Quality, Timely, Cost-effective solutions for specialty fastener applications. Every product is built to your specifications, using your prints if necessary.
Below are the technical specifications of the Silicon Bronze 651 Bar Stock we have available to meet your needs.
Low-silicon bronze B, UNS C65100, OSO35 Temper rod
Subcategory: Bronze; Copper Alloy; Metal; Nonferrous Metal Key Words: CDA 651, ISO CuSi1, CEN C115C
| Component | Wt. % |
| Cu | 98.5 |
| Fe | Max 0.8 |
| Mn | Max 0.7 |
| Pb | Max 0.05 |
| Si | 0.8 – 2 |
| Zn | Max 1.5 |
Material Notes: Good to excellent corrosion resistance. Excellent hot and cold workability. Fabricated by forming and bending, heading and upsetting, hot forging and pressing, roll threading and knurling, squeezing and swaging. Applications: hydraulic pressure lines, anchor screws, bolts, cable clamps, cap screws, machine screws, marine hardware, nuts, pole-line hardware, rivets, U-bolts, electrical conduits, heat exchanger tubing, welding rod.
Test specimen: rod – 25mm diameter.
| Physical Properties | Metric | English | Comments |
| Density | 8.75 g/cc | 0.316 lb/in³ | at 20°C (68°F) |
| Mechanical Properties | |||
| Hardness, Rockwell F | 55 | 55 | |
| Tensile Strength, Ultimate | 275 MPa | 39900 psi | |
| Tensile Strength, Yield | 105 MPa | 15200 psi | 0.5% extension under load |
| Elongation at Break | 50 % | 50 % | In 50 mm |
| Modulus of Elasticity | 115 GPa | 16700 ksi | |
| Machinability | 30 % | 30 % | UNS C36000 (free-cutting brass) = 100% |
| Shear Modulus | 44 GPa | 6380 ksi | |
| Electrical Properties | |||
| Electrical Resistivity | 1.44e-005 ohm-cm | 1.44e-005 ohm-cm | |
| Thermal Properties | |||
| CTE, linear 250°C | 18 µm/m-°C | 10 µin/in-°F | from 20-300°C (68-570°F) |
| Heat Capacity | 0.38 J/g-°C | 0.0908 BTU/lb-°F | |
| Thermal Conductivity | 57 W/m-K | 396 BTU-in/hr-ft²-°F | at 20°C (68°F) |
| Melting Point | 1030 – 1060 °C | 1890 – 1940 °F | |
| Solidus | 1030 °C | 1890 °F | |
| Liquidus | 1060 °C | 1940 °F | |
| Processing Properties | |||
| Annealing Temperature | 475 – 675 °C | 887 – 1250 °F | |
| Hot-Working Temperature | 700 – 875 °C | 1290 – 1610 °F | |
References are available for this material.